 note = {P(論文), The surface layer of an Al-3mass%Mg alloy annealed at high temperature and its effect on the fatigue strength were studied by measurements of microhardness, electrical resistivity and number of cycles to failure under repeated tensile loading. The results obtained are summarized as follows. (1) The surface layer was softer than the interior. The thickness of this layer was about 50 μm. (2) It is isterpreted that the formation of this soft surface layer was becaused by the depletion of Mg atoms due to oxidation of Mg atoms near surface. (3) The soft surface layer has an effect of rasing the fatigue strength to repetitive tensile loading.},