硬質塩化ビニルのせん断加工におけるせん断クラック発生ならびに成長時のひずみ分布
https://ous.repo.nii.ac.jp/records/785
https://ous.repo.nii.ac.jp/records/785d08db79b-a45f-453b-beb6-7d35841b59d8
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
KJ00000063338.pdf (620.3 kB)
|
|
| Item type | 紀要論文(ELS) / Departmental Bulletin Paper(1) | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 1988-03-20 | |||||||||||
| タイトル | ||||||||||||
| タイトル | 硬質塩化ビニルのせん断加工におけるせん断クラック発生ならびに成長時のひずみ分布 | |||||||||||
| 言語 | ja | |||||||||||
| タイトル | ||||||||||||
| タイトル | Strain Distribution on Initiation and Propagation of Crack in PVC Shearing Process | |||||||||||
| 言語 | en | |||||||||||
| タイトル | ||||||||||||
| タイトル | コウシツ エンカ ビニル ノ センダン カコウ ニオケル センダン クラック ハッセイ ナラビニ セイチョウジ ノ ヒズミ ブンプ | |||||||||||
| 言語 | ja-Kana | |||||||||||
| 言語 | ||||||||||||
| 言語 | jpn | |||||||||||
| 資源タイプ | ||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||||||
| 資源タイプ | departmental bulletin paper | |||||||||||
| ページ属性 | ||||||||||||
| 内容記述タイプ | Other | |||||||||||
| 内容記述 | P(論文) | |||||||||||
| 著者名 |
金枝, 敏明
× 金枝, 敏明
|
|||||||||||
| 著者所属(日) | ||||||||||||
| ja | ||||||||||||
| 岡山理科大学機械工学科 | ||||||||||||
| 著者所属(英) | ||||||||||||
| en | ||||||||||||
| Department of Mechanical Engineering, Okayama University of Science | ||||||||||||
| 抄録(英) | ||||||||||||
| 内容記述タイプ | Other | |||||||||||
| 内容記述 | Sheared surfaces of Polyvinylchloride (PVC) are not smooth as expected, although the strength is lower than that of conventional metals. The shearing mechanism for PVC has been studied by using a machining set up in a scanning electron microscope (SEM). A visio-plasticity method is used to investigate strain distribution of the work. The direct SEM observation results show that shearing phenomenon of PVC is different from that of conventional metals, because of shape of the crack in the shearing process. The punch side crack initiates on the severely domed surface. The fracture mode of the initiating crack is mode I (opening crack tip) and that of the propagating crack is mode II (shearing on plane). The strain distribution calculated by the method shows that the punch side crack initiates along the maximum principal strain rate direction and propagates along the maximum shear strain rate direction. On the other hand, the die side crack also initiates along the maximum principal strain rate direction and may propagates along the maximum shear strain rate direction. | |||||||||||
| 言語 | en | |||||||||||
| 雑誌書誌ID | ||||||||||||
| 収録物識別子タイプ | NCID | |||||||||||
| 収録物識別子 | AN00033244 | |||||||||||
| 書誌情報 |
ja : 岡山理科大学紀要. A, 自然科学 en : Bulletin of Okayama University of Science. A, Natural Sciences 巻 23, p. 91-103, 発行日 1988-03-20 |
|||||||||||